Raw material recycling Film waste recycling raw material LLDPE

1. LLDPE film gradeTestsValueUnitMelt Flow Rate (MFR)2.0±0.4g/10minDensity920±2Kg/cm3Tensile Strength at Yield8Mpa ≥Tensile Strength at Break12Mpa ≥haze15%≤PackingIn 25 kg PP woven bags,20MT/20\'FCL  2.

Featured Products

1. LLDPE film grade
TestsValueUnit
Melt Flow Rate (MFR)2.0±0.4g/10min
Density920±2Kg/cm3
Tensile Strength at Yield8Mpa ≥
Tensile Strength at Break12Mpa ≥
haze15%≤
PackingIn 25 kg PP woven bags,20MT/20'FCL
  
2. LLDPE for Master Batch Use 
TestsValueUnit
Melt Flow Rate (MFR)20g/10min
Density0.924g/cm3
Tensile StrengthMD12Mpa
TD 10
Elongation at Yield13%
Elongation at Break200
Dark Drop Impact105g
Brittle Temperature(F 50)-70°C
Vicat Softening Point90°C
PackingIn 25 kg woven bags,20MT/20'FCL
 
3. LLDPE Powder Rotational Molding Grade for Tank Use
TestsValueUnit
Melt Flow Rate (MFR)3.2g/10min
Density0.939g/cm3
Melting Point127°C
Tensile Yield Strength21Mpa
Tensile Strength at Break28Mpa
Elongation at Break1,100%
Flexural Modulus750Mpa
Brittle Temperature<-60°C
 

Main Applications
LLDPE is mainly used for making film, pipes, injection-molding products, blow-molding containers, rotationally-molding products and wire & cable covering material.

Raw Material Recycled Film Scrap Recycling Raw Material LLDPERaw Material Recycled Film Scrap Recycling Raw Material LLDPERaw Material Recycled Film Scrap Recycling Raw Material LLDPERaw Material Recycled Film Scrap Recycling Raw Material LLDPERaw Material Recycled Film Scrap Recycling Raw Material LLDPERaw Material Recycled Film Scrap Recycling Raw Material LLDPE

 